ATI 18CrCb™ |
|---|
| UNS Number: S44100 | | Forms: Sheet; | | Form Properties Shown: | | | Composition nominal wt%: | N 0.03 max, Cb 0.3+(9xC) min - 0.90 max, Ti 0.10 min - 0.50 max, Ni 1.00 max, Cr 17.5 min - 19.5 max, Si 1.00 max, S 0.03 max, P 0.04 max, Mn 1.00 max, C 0.03 max |
| | Specifications: | Contact us for information. | | Density lb/in3(g/cm3): | 0.278 (7.70) | | Tensile Strength ksi(MPa): | 60 min (414 min) | | 0.2% Yield Strength ksi(MPa): | 35 min (241 min) | | Elongation%: | 20% min | | Hardness: | 90 HRB max |
| | End Use Market(s): Automotive |
ATI 409 Cb™ |
|---|
| UNS Number: S41045 | | Forms: Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | Cb 9x(C+N) min - 0.60 max, N 0.030 max, Ni 0.50 max, Cr 12.0 min - 13.0 max, Si 1.00 max, S 0.030 max, P 0.040 max, Mn 1.00 max, C 0.030 max, Fe balance Cb 9x(C+N) min - 0.60 max, N 0.030 max, Ni 0.50 max, Cr 12.0 min - 13.0 max, Si 1.00 max, S 0.030 max, P 0.040 max, Mn 1.00 max, C 0.030 max, Fe balance |
| | Specifications: | ASTM A240 ASTM A240 | | Density lb/in3(g/cm3): | 0.280 (7.75) 0.280 (7.75) | | Tensile Strength ksi(MPa): | 55 min (380 min) 55 min (380 min) | | 0.2% Yield Strength ksi(MPa): | 30 min (205 min) 30 min (205 min) | | Elongation%: | 22% min 22% min | | Hardness: | 80 HRB max 80 HRB max |
| | End Use Market(s): Automotive |
ATI 409HP™ |
|---|
| UNS Number: S40900/S40910/S40920/S40930 | | Forms: Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | (Ti+Cb) [0.08+8x(C+N)] min - 0.75 max, Ti 0.05 min - 0.75 max, N 0.030 max, Ni 0.50 max, Cr 10.5 min - 11.7 max, Si 1.00 max, S 0.020 max, P 0.040 max, Mn 1.00 max, C 0.030 max, Fe balance (Ti+Cb) [0.08+8x(C+N)] min - 0.75 max, Ti 0.05 min - 0.75 max, N 0.030 max, Ni 0.50 max, Cr 10.5 min - 11.7 max, Si 1.00 max, S 0.020 max, P 0.040 max, Mn 1.00 max, C 0.030 max, Fe balance |
| | Specifications: | ASTM A240, ASME SA-240 ASTM A240, ASME SA-240 | | Density lb/in3(g/cm3): | 0.280 (7.75) 0.280 (7.75) | | Tensile Strength ksi(MPa): | 55 min (380 min) 55 min (380 min) | | 0.2% Yield Strength ksi(MPa): | 25 min (170 min) 25 min (170 min) | | Elongation%: | 20% min 20% min | | Hardness: | 88 HRB max 88 HRB max |
| | End Use Market(s): Automotive, Chemical Processing, Electrical Energy, Food Equipment & Appliances |
ATI 410S™ |
|---|
| UNS Number: S41008 | | Forms: Plate; Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | Ni 0.60 max, Cr 11.5 min - 13.5 max, Si 1.00 max, S 0.030 max, P 0.040 max, Mn 1.00 max, C 0.08 max, Fe balance Ni 0.60 max, Cr 11.5 min - 13.5 max, Si 1.00 max, S 0.030 max, P 0.040 max, Mn 1.00 max, C 0.08 max, Fe balance Ni 0.60 max, Cr 11.5 min - 13.5 max, Si 1.00 max, S 0.030 max, P 0.040 max, Mn 1.00 max, C 0.08 max, Fe balance |
| | Specifications: | ASTM A240 ASTM A240 ASTM A240 | | Density lb/in3(g/cm3): | 0.280 (7.75) 0.280 (7.75) 0.280 (7.75) | | Tensile Strength ksi(MPa): | 60 min (415 min) 60 min (415 min) 60 min (415 min) | | 0.2% Yield Strength ksi(MPa): | 30 min (205 min) 30 min (205 min) 30 min (205 min) | | Elongation%: | 22% min 22% min 22% min | | Hardness: | 89 HRB max 89 HRB max 89 HRB max |
| | End Use Market(s): Automotive, Chemical Processing, Electrical Energy |
ATI 412™ |
|---|
| UNS Number: S41003 | | Forms: Plate; Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | N 0.030 max, Ni 1.50 max, Cr 10.5 min - 12.5 max, S 0.030 max, P 0.040 max, Si 1.00 max, Mn 1.50 max, C 0.030 max, Fe balance N 0.030 max, Ni 1.50 max, Cr 10.5 min - 12.5 max, S 0.030 max, P 0.040 max, Si 1.00 max, Mn 1.50 max, C 0.030 max, Fe balance N 0.030 max, Ni 1.50 max, Cr 10.5 min - 12.5 max, S 0.030 max, P 0.040 max, Si 1.00 max, Mn 1.50 max, C 0.030 max, Fe balance |
| | Specifications: | ASTM A240 ASTM A240 ASTM A240 | | Density lb/in3(g/cm3): | 0.280 (7.75) 0.280 (7.75) 0.280 (7.75) | | Tensile Strength ksi(MPa): | 66 min (455 min) 66 min (455 min) 66 min (455 min) | | 0.2% Yield Strength ksi(MPa): | 40 min (275 min) 40 min (275 min) 40 min (275 min) | | Elongation%: | 18% min 18% min 18% min | | Hardness: | 20 HRC max 20 HRC max 20 HRC max |
| | End Use Market(s): Transportation, Construction and Mining |
ATI 430 |
|---|
| UNS Number: S43000 | | Forms: Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | P 0.040 max, S 0.030 max, Ni 0.75 max, Cr 16.0 min - 18.0 max, Si 1.00 max, Mn 1.00 max, C 0.12 max, Fe balance P 0.040 max, S 0.030 max, Ni 0.75 max, Cr 16.0 min - 18.0 max, Si 1.00 max, Mn 1.00 max, C 0.12 max, Fe balance |
| | Specifications: | ASTM A240 ASTM A240 | | Density lb/in3(g/cm3): | 0.278 (7.70) 0.278 (7.70) | | Tensile Strength ksi(MPa): | 65 min (450 min) 65 min (450 min) | | 0.2% Yield Strength ksi(MPa): | 30 min (205 min) 30 min (205 min) | | Elongation%: | 22% min 22% min | | Hardness: | 89 HRB max 89 HRB max |
| | End Use Market(s): Food Equipment & Appliances, Construction and Mining |
ATI 430 Ti™ |
|---|
| UNS Number: S43036 | | Forms: Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | Ti (5xC) min - 0.75 max, Ni 0.75 max, Cr 16.0 min - 19.5 max, Si 1.00 max, S 0.030 max, P 0.40 max, Mn 1.00 max, C 0.10 max, Fe balance Ti (5xC) min - 0.75 max, Ni 0.75 max, Cr 16.0 min - 19.5 max, Si 1.00 max, S 0.030 max, P 0.40 max, Mn 1.00 max, C 0.10 max, Fe balance |
| | Specifications: | ASTM A959 ASTM A240, A959 | | Density lb/in3(g/cm3): | 0.278 (7.70) 0.278 (7.70) | | Tensile Strength ksi(MPa): | 60 min (415 min) 60 min (415 min) | | 0.2% Yield Strength ksi(MPa): | 30 min (205 min) 30 min (205 min) | | Elongation%: | 20% min 20% min | | Hardness: | Contact us for information. Contact us for information. |
| | End Use Market(s): Chemical Processing, Automotive |
ATI 433™ |
|---|
| UNS Number: S44500 | | Forms: Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | Cb 10x(C+N) min - 0.80 max, Cu 0.30 min - 0.60 max, N 0.03 max, Ni 0.60 max, Cr 19.0 min - 21.0 max, Si 1.00 max, S 0.012 max, P 0.040 max, Mn 1.00 max, C 0.020 max, Fe balance Cb 10x(C+N) min - 0.80 max, Cu 0.30 min - 0.60 max, N 0.03 max, Ni 0.60 max, Cr 19.0 min - 21.0 max, Si 1.00 max, S 0.012 max, P 0.040 max, Mn 1.00 max, C 0.020 max, Fe balance |
| | Specifications: | ASTM A240 ASTM A240 | | Density lb/in3(g/cm3): | 0.280 (7.75) 0.280 (7.75) | | Tensile Strength ksi(MPa): | 62 min (427 min) 62 min (427 min) | | 0.2% Yield Strength ksi(MPa): | 30 min (205 min) 30 min (205 min) | | Elongation%: | 22% min 22% min | | Hardness: | 83 HRB max 83 HRB max |
| | End Use Market(s): Automotive |
ATI 436S™ |
|---|
| UNS Number: ... | | Forms: Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | Ti 8x(C+N) min - 0.80 max, N 0.020 max, Mo 0.75 min - 1.50 max, Ni 0.60 max, Cr 17.0 min - 19.0 max, Si 0.60 max, S 0.020 max, P 0.040 max, Mn 0.50 max, C 0.025 max, Fe balance Ti 8x(C+N) min - 0.80 max, N 0.020 max, Mo 0.75 min - 1.50 max, Ni 0.60 max, Cr 17.0 min - 19.0 max, Si 0.60 max, S 0.020 max, P 0.040 max, Mn 0.50 max, C 0.025 max, Fe balance |
| | Specifications: | Contact us for information. Contact us for information. | | Density lb/in3(g/cm3): | 0.280 (7.75) 0.280 (7.75) | | Tensile Strength ksi(MPa): | 60 min (415 min) 60 min (415 min) | | 0.2% Yield Strength ksi(MPa): | 35 min (240 min) 35 min (240 min) | | Elongation%: | 20% min 20% min | | Hardness: | Contact us for information. Contact us for information. |
| | End Use Market(s): Automotive |
ATI 439 HP™ |
|---|
| UNS Number: S43035 | | Forms: Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | Al 0.15 max, Ti [0.20+4x(C+N)] min - 1.10 max, N 0.030 max, Ni 0.50 max, Cr 17.0 min - 19.0 max, Si 1.00 max, S 0.030 max, P 0.040 max, Mn 1.00 max, C 0.030 max, Fe balance Al 0.15 max, Ti [0.20+4x(C+N)] min - 1.10 max, N 0.030 max, Ni 0.50 max, Cr 17.0 min - 19.0 max, Si 1.00 max, S 0.030 max, P 0.040 max, Mn 1.00 max, C 0.030 max, Fe balance |
| | Specifications: | ASTM A240 ASTM A240 | | Density lb/in3(g/cm3): | 0.278 (7.71) 0.278 (7.71) | | Tensile Strength ksi(MPa): | 60 min (415 min) 60 min (415 min) | | 0.2% Yield Strength ksi(MPa): | 30 min (205 min) 30 min (205 min) | | Elongation%: | 22% min 22% min | | Hardness: | 89 HRB max 89 HRB max |
| | End Use Market(s): Automotive, Electrical Energy, Chemical Processing, Food Equipment & Appliances |
ATI 439™ |
|---|
| UNS Number: S43035 | | Forms: Bar; Rod; Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | P 0.040 max, S 0.030 max, Ti [0.20+4x(C+N)] min - 1.10 max, Al 0.15 max, N 0.030 max, Ni 0.50 max, Cr 17.0 min - 19.0 max, Si 1.00 max, Mn 1.00 max, C 0.030 max, Fe balance P 0.040 max, S 0.030 max, Ti [0.20+4x(C+N)] min - 1.10 max, Al 0.15 max, N 0.030 max, Ni 0.50 max, Cr 17.0 min - 19.0 max, Si 1.00 max, Mn 1.00 max, C 0.030 max, Fe balance C 0.030 max, Mn 1.00 max, P 0.040 max, S 0.030 max, Si 1.00 max, Cr 17.0 min - 19.0 max, Ni 0.50 max, N 0.030 max, Ti [0.20+4x(C+N)] min - 1.10 max, Al 0.15 max, Fe balance C 0.030 max, Mn 1.00 max, P 0.040 max, S 0.030 max, Si 1.00 max, Cr 17.0 min - 19.0 max, Ni 0.50 max, N 0.030 max, Ti [0.20+4x(C+N)] min - 1.10 max, Al 0.15 max, Fe balance |
| | Specifications: | ASIM A240, ASME SA240 ASTM A240, ASME SA-240 ASTM A240 ASTM A240 | | Density lb/in3(g/cm3): | 0.278 (7.70) 0.278 (7.70) 0.278 (7.71) 0.278 (7.71) | | Tensile Strength ksi(MPa): | 60 min (415 min) 60 min (415 min) 60 min (415 min) 60 min (415 min) | | 0.2% Yield Strength ksi(MPa): | 30 min (205 min) 30 min (205 min) 30 min (205 min) 30 min (205 min) | | Elongation%: | 22% min 22% min 22% min 22% min | | Hardness: | 89 HRB max 89 HRB max 89 HRB max 89 HRB max |
| | End Use Market(s): Automotive, Electrical Energy, Chemical Processing, Food Equipment & Appliances.
Automotive Exhaust, Manifolds and Mufflers, Residential Furnace Primary Heat Exchangers, Direct-Fired Hot Water Tanks, Heat Exchanger Tubing. |
ATI 441 HP™ |
|---|
| UNS Number: S44100 | | Forms: Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | N 0.03 max, Cb 0.3+(9xC) min - 0.9 max, Ti 0.1 min - 0.5 max, Ni 1.00 max, Cr 17.5 min - 19.5 max, Si 1.00 max, S 0.03 max, P 0.04 max, Mn 1.00 max, C 0.03 max, Fe balance C 0.03 max, Mn 1.00 max, N 0.03 max, P 0.04 max, S 0.03 max, Si 1.00 max, Cr 17.5 min - 19.5 max, Ni 1.00 max, Ti 0.1 min - 0.5 max, Cb 0.3+(9xC) min - 0.9 max, Fe balance |
| | Specifications: | Contact us for information. Contact us for information. | | Density lb/in3(g/cm3): | 0.278 (7.71) 0.278 (7.71) | | Tensile Strength ksi(MPa): | 60 min (414 min) 60 min (414 min) | | 0.2% Yield Strength ksi(MPa): | 35 min (241 min) 35 min (241 min) | | Elongation%: | 20% min 20% min | | Hardness: | 90 HRB max 90 HRB max |
| | End Use Market(s): Electrical Energy, Automotive, Food Equipment & Appliances |
ATI 444™ |
|---|
| UNS Number: S44400 | | Forms: Plate; Sheet; Strip; | | Form Properties Shown: | | | Composition nominal wt%: | (Ti+Cb) [0.20+4x(C+N)] min - 0.80 max, N 0.040 min - 0.070 max, Mo 1.75 min - 2.50 max, Ni 1.00 max, Cr 17.5 min - 19.5 max, Si 1.00 max, S 0.030 max, P 0.040 max, Mn 1.00 max, C 0.025 max (Ti+Cb) [0.20+4x(C+N)] min - 0.80 max, N 0.035 max, Mo 1.75 min - 2.50 max, Ni 1.00 max, Cr 17.5 min - 19.5 max, Si 1.00 max, S 0.030 max, P 0.040 max, Mn 1.00 max, C 0.025 max (Ti+Cb) [0.20+4x(C+N)] min - 0.80 max, N 0.035 max, Mo 1.75 min - 2.50 max, Ni 1.00 max, Cr 17.5 min - 19.5 max, Si 1.00 max, S 0.030 max, P 0.040 max, Mn 1.00 max, C 0.025 max |
| | Specifications: | ASTM A240, ASME SA-240 ASTM A240, ASME SA-240 ASTM A240, ASME SA-240, SA 268 | | Density lb/in3(g/cm3): | 0.280 (7.75) 0.280 (7.75) 0.280 (7.75) | | Tensile Strength ksi(MPa): | 60 min (415 min) 60 min (415 min) 60 min (415 min) | | 0.2% Yield Strength ksi(MPa): | 40 min (275 min) 40 min (275 min) 40 min (275 min) | | Elongation%: | 20% min 20% min 20% min | | Hardness: | 96 HRB max 96 HRB max 96 HRB max |
| | End Use Market(s): Automotive, Food Equipment & Appliances, Chemical Processing |
OHMALOY® 30 |
|---|
| UNS Number: K91470 | | Forms: Strip; | | Form Properties Shown: | | | Composition nominal wt%: | Ti 0.30 typical, Al 3.00 typical, Cr 13.0 typical, Si 0.30 typical, Mn 0.35 typical, C 0.025 typical, Fe balance |
| | Specifications: | Contact us for information. | | Density lb/in3(g/cm3): | 0.270 (7.48) | | Tensile Strength ksi(MPa): | 76 typical (524 typical) | | 0.2% Yield Strength ksi(MPa): | 55 typical (379 typical) | | Elongation%: | 28% typical | | Hardness: | 88 HRB typical |
| | End Use Market(s): Construction and Mining, Transportation |
OHMALOY® 40 |
|---|
| UNS Number: K91670 | | Forms: Strip; | | Form Properties Shown: | | | Composition nominal wt%: | Ti 0.3 typical, Al 3.95 typical, Cr 13.0 typical, Si 0.3 typical, Mn 0.35 typical, C 0.025 typical, Fe balance |
| | Specifications: | Contact us for information. | | Density lb/in3(g/cm3): | 0.267 (7.41) | | Tensile Strength ksi(MPa): | 87 typical (600 typical) | | 0.2% Yield Strength ksi(MPa): | 65 typical (448 typical) | | Elongation%: | 23% typical | | Hardness: | 88 HRB typical |
| | End Use Market(s): Construction and Mining, Transportation |
|
|