ATI HX^™

UNS N06002

Product Documents

Data Sheet English (PDF)

Product Specifications By Form

Bar

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Cr		21.75
Fe		18.5
Mo		9.0
Co		1.5
W		0.6
C		0.1
Ni	Balance

Density

lb/in³	g/cm³
0.297	8.45

Tensile Strength

ksi	MPa
100 min	690 min

Yield Strength

ksi	MPa
40 min	276 min

Hardness

80 HRB max

Elongation

40% min

Billet

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Cr		21.75
Fe		18.5
Mo		9.0
Co		1.5
W		0.6
C		0.1
Ni	Balance

Density

lb/in³	g/cm³
0.297	8.45

Tensile Strength

ksi	MPa
100 min	690 min

Yield Strength

ksi	MPa
40 min	276 min

Hardness

80 HRB max

Elongation

40% min

Plate

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Cr	20.5	23.0
Fe	17.0	20.0
Mo	8.0	10.0
Co	0.5	2.5
W	0.2	1.0
Mn		1.0
Si		1.0
C	0.05	0.15
P		0.04
S		0.03

Density

lb/in³	g/cm³
0.297	8.28

Tensile Strength

ksi	MPa
95 min	655 min

Yield Strength

ksi	MPa
35 min	240 min

Elongation

35% min

Specifications

ASTM B435, ASME SB-435, AMS 5536

Sheet

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Cr	20.5	23.0
Fe	17.0	20.0
Mo	8.0	10.0
Co	0.5	2.5
W	0.2	1.0
Mn		1.0
Si		1.0
C	0.05	0.15
P		0.04
S		0.03

Density

lb/in³	g/cm³
0.297	8.28

Tensile Strength

ksi	MPa
95 min	655 min

Yield Strength

ksi	MPa
35 min	240 min

Elongation

35% min

Specifications

ASTM B435, ASME SB-435, AMS 5536

Strip

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Cr	20.5	23.0
Fe	17.0	20.0
Mo	8.0	10.0
Co	0.5	2.5
W	0.2	1.0
Mn		1.0
Si		1.0
C	0.05	0.15
P		0.04
S		0.03

Density

lb/in³	g/cm³
0.297	8.28

Tensile Strength

ksi	MPa
95 min	655 min

Yield Strength

ksi	MPa
35 min	240 min

Elongation

35% min

Specifications

ASTM B435, ASME SB-435, AMS 5536